DLT330-2010非正式版水电水利工程金属结构及设备焊接接头衍射时差法超生检测非正式版.pdf 24页

'DL/T330—2010目次前言··································································································································································Ⅱ1范围·····························································································································································12规范性引用文件··········································································································································13术语和定义··················································································································································14一般规定······················································································································································35检测系统······················································································································································56试块·····························································································································································57检验等级······················································································································································78检测准备······················································································································································79检测系统设置和校准··································································································································910检测·························································································································································1011检测数据分析···········································································································································1112对非平行扫查发现的相关显示的辅助检测···························································································1213缺欠评定··················································································································································1314检测记录和报告······································································································································13附录A（资料性附录）水电水利工程常用非合金钢、低合金钢和合金钢···············································14附录B（资料性附录）参考试块·················································································································15附录C（资料性附录）缺欠深度、高度及表面盲区高度的计算······························································17附录D（资料性附录）常见焊接缺欠TOFD图像·····················································································18附录E（资料性附录）焊缝衍射时差法超声检测报告··············································································22I DL/T330—2010前言衍射时差法超声检测技术作为一种独立的无损检测方法，具有环保、对人体无伤害、缺欠检出率高、缺欠尺寸定量精度高、检测结果能图像化存储和便于实现自动扫查等优点，目前该项检测技术已经在许多大型水电站的焊缝检测中应用。本标准起草过程中通过调研、收集资料、对比试验、实践验证和分析归纳，并结合水电水利工程的特点，明确了水电水利工程金属结构及设备焊接接头衍射时差法超声检测的方法及缺欠评定要求。本标准由中国电力企业联合会提出并归口。本标准起草单位：国电大渡河流域水电开发有限公司、华电郑州机械设计研究院有限公司。本标准主要起草人：黄张豪、曹麦对、胡卫、刘雪芳、李林、杨兴斌、姚福明、王富林、李剑君、高景荣、熊剑鸣、陈刘辉、雷清华。本标准在执行过程中的意见或建议反馈至中国电力企业联合会标准化管理中心（北京市白广路二条一号，100761）。II标准分享网www.bzfxw.com免费下载 DL/T330—2010水电水利工程金属结构及设备焊接接头衍射时差法超声检测1范围本标准规定了水电水利工程金属结构及设备焊接接头衍射时差法超声检测的方法及缺欠评定要求。本标准适用于母材厚度为12mm～400mm的工程结构用非合金钢、低合金钢和合金钢对接焊接接头衍射时差法超声检测。其他类型金属材料可参照执行。2规范性引用文件下列文件对本文件是必不可少的。凡是注日期的引用文件，仅注日期的版本适用于本文件。凡是不注日期的引用文件，其最新版本（包括所有的修改单）适用于本文件。GB/T19799.1超声探伤用1号标准试块技术条件JB/T10061A型脉冲反射式超声波探伤仪通用技术条件3术语和定义下列术语和定义适用于本标准。3.1www.bzfxw.com衍射时差法超声检测TOFDTimeofFlightDiffractiontechnique利用缺欠端点的衍射波信号发现缺欠和测定缺欠尺寸的一种超声检测方法，一般使用纵波斜探头，采用一发一收模式，见图1。3.2直通波lateralwave从发射探头沿工件以最短路径到达接收探头的超声波，见图1。3.3底面反射波backwallecho经底面反射到接收探头的超声波，见图1。3.4坐标定义coordinatedefinition规定检测起始参考点O点以及X、Y和Z坐标的含义，见图2。3.5探头中心间距PCSprobecenterseparation发射探头和接收探头入射点之间的距离，见图3。3.6缺欠上端点uppertipofimperfection距扫查面最近的缺欠端点，见图3。3.7缺欠下端点lowertipofimperfection距扫查面最远的缺欠端点，见图3。1 www.bzfxw.com标准分享网www.bzfxw.com免费下载 DL/T330—20103.8缺欠深度imperfectiondepth缺欠上端点与扫查面间的距离，见图3中的d1。3.9缺欠高度imperfectionheight在一个缺欠长度范围内，缺欠最高上端点与最低下端点在工件厚度方向上的投影距离，其中扫查面开口缺欠高度指缺欠下端点到扫查面的距离，底面开口缺欠高度指缺欠上端点到底面的距离，见图3中的h。3.10A扫描显示A-scandisplay超声波信号的射频波形显示图，一个轴代表波幅，另一个轴代表声波的传播时间。3.11TOFD图像TOFDimageTOFD数据的二维显示，是将扫查过程中采集的A扫描信号连续拼接而成，一个轴代表探头移动距离，另一个轴代表深度，一般用灰度表示A扫描信号的幅度。3.12非平行扫查non-parallelscan探头运动方向与声束方向成直角的扫查方式。也叫D扫描，见图4a）。3.13平行扫查parallelscan探头运动方向与声束方向平行的扫查方式。也叫B扫描，见图4b）。3.14www.bzfxw.com偏置非平行扫查offsetnon-parallelscan在焊缝TOFD检测时，探头组主声束的交点偏离焊缝中心线的非平行扫查，见图4c）。3.15纵向平行扫查portraitscan焊缝TOFD检测时，探头组沿着焊缝方向移动的平行扫查，见图5。3.16横向非平行扫查horizontalnon-parallelscan焊缝TOFD检测时，探头组垂直于焊缝方向移动的非平行扫查，见图6。4一般规定4.1人员按照本标准进行TOFD检测、分析图像和出具报告的人员，应取得电力行业或中国无损检测学会等超声检测2级及以上资格证书和TOFD检测2级及以上专项资格证书。4.2材料本标准TOFD检测适用的材料范围参见附录A，其他金属材料在充分考虑材料的几何特性、声学特性和检测灵敏度影响的前提下可参照执行。4.3检测工艺检测前应针对被检工件的材质、厚度、坡口形式、结构特点、施工环境，以及本标准的有关要求编制检测工艺。3 www.bzfxw.com标准分享网www.bzfxw.com免费下载 DL/T330—20101—参考线；2—探头移动的方向；3—发射探头；4—接收探头图6横向非平行扫查5检测系统5.1检测设备5.1.1TOFD检测设备应具有线性A扫描显示，超声波发射和接收，数据自动采集、记录和显示，信号分析等功能。根据需要可使用单通道或多通道设备。5.1.2设备性能满足以下要求：a）A扫描水平线性误差不大于1％，垂直线性误差不大于5％。b）脉冲接收器带宽应大于等于探头公称的频率带宽。c）增益应在80dB以上，其步进级小于等于1dB，且连续可调。d）数字采样率至少为4倍探头公称频率，若需对原始数据进行数字信号处理，采样率应增加到探头公称频率的8倍。5.1.3设备其余指标应符合www.bzfxw.comJB/T10061的规定。5.2探头用于TOFD检测的超声探头应满足以下要求：a）探头的波形模式为纵波。b）探头类型可以选用单晶片或相控阵探头、非聚焦或聚焦探头。c）探头对中两个探头中心频率偏差不大于20％。d）探头对中两个探头应具有相同的晶片尺寸。e）在信号峰值下降20dB处测得的探头脉冲持续时间不得超过两个周期。f）连续发射脉冲的声信号间无干扰产生。5.3扫查装置扫查装置应保证扫查时两探头入射点间距相对稳定，使探头与扫查面耦合良好。扫查装置可以采用动力或人工驱动。扫查装置上应安装位置编码器。5.4数据采集、记录和显示系统数据采集、记录和显示系统应具备以下功能：a）应当采用自动的计算机数据采集装置，原始数据应自动记录且不可更改。b）可自动形成扫描图形。c）至少应记录和显示A扫描信号，以及指示波形与其相邻波形之间相对位置的信息。d）设备应具有检测数据的存取功能。6试块6.1校准试块校准试块采用GB/T19799.1中的1号试块，用于仪器、探头、系统性能校准和检测校准。5 www.bzfxw.com标准分享网www.bzfxw.com免费下载 DL/T330—20107检验等级7.1检验等级的分级根据质量要求检验等级分为A、B两级，A级为普通级，B级为优化级。A级检验应进行单面扫查，必要时双面扫查；B级检验应进行双面扫查。7.2检验等级的检验范围7.2.1A级检验适用于母材厚度小于50mm的二类焊缝。7.2.2B级检验适用于一类焊缝和母材厚度不小于50mm的二类焊缝。8检测准备8.1检测区域检测区的宽度应是焊缝本身，再加上焊缝两侧各相当于母材厚度30％的一段区域，这个区域最小为5mm，最大为20mm。8.2扫查面8.2.1探头移动区应清除焊接飞溅、铁屑、油垢及其他杂质。8.2.2检测表面应平整，便于探头的移动，其表面粗糙度Ra值应不大于6.3µm。8.2.3要求去除余高的焊缝，应将余高打磨到与邻近母材平齐；保留余高的焊缝，如果焊缝表面有咬边、较大的隆起和凹陷等也应进行适当的修磨，并作圆滑过渡。其他影响信号采集的因素均应消除。8.2.4平行扫查时应将焊缝余高磨平。8.3厚度方向分区8.3.1当被检工件厚度不大于50mm时，可不进行分区。8.3.2当被检工件厚度大于www.bzfxw.com50mm时，应在厚度方向分成若干区域采用不同的探头对进行检测。8.3.3厚度分区和检测参数推荐设置见表2。表2厚度分区及检测参数推荐设置表厚度TTOFD分区深度覆盖中心频率晶片直径主声束主声束角度θmm分区范围MHzmm聚焦深度H12～3510～T10～570°～60°2～62T/335～5010～T5～370°～60°3～62T/310～T/25～370°～60°3～62T/650～1002T/2～T5～360°～45°6～125T/610～T/35～370°～60°3～62T/9100～2002T/3～2T/35～360°～45°6～125T/932T/3～T5～260°～45°6～208T/910～T/45～370°～60°3～62T/122T/4～T/25～360°～45°6～125T/12200～3003T/2～3T/45～260°～45°6～208T/1243T/4～T3～150°～45°10～2011T/1210～T/55～370°～60°3～62T/152T/5～2T/55～360°～45°6～125T/15300～40032T/5～3T/55～260°～45°6～208T/1543T/5～4T/53～150°～45°10～2011T/1554T/5～T3～150°～45°12～2514T/157 DL/T330—20108.4探头选择8.4.1探头选择应保证完全覆盖检测区域和获得最佳的检测效果。8.4.2检测时推荐使用非聚焦探头，需要改善定量分辨力时宜使用聚焦探头。8.4.3探头晶片直径、中心频率和主声束角度选择见表2。8.4.4当被检材料晶粒结构有明显变化时，为保证足够的穿透力或提高分辨力宜使用其他频率的探头。8.5PCS值设置8.5.1非平行扫查时，不需要分区的工件检测，PCS值设置为使探头对的声束轴线交点位于工件厚度的2/3处，声束交叉角为110°～120°；需要分区的工件检测，PCS值设置为使声束交叉点位于每个检测区域厚度方向的2/3处。8.5.2对于已知缺欠或疑似缺欠部位的扫查，将PCS值设置为使探头对的声束轴线交点在该部位。8.5.3对两侧母材厚度不等的焊缝检测应根据两侧母材厚度分别设置PCS1值（小间距）和PCS2值（大间距）。8.6扫查方式选择8.6.1扫查方式一般选用非平行扫查。用于缺欠的快速探测，以及缺欠长度、缺欠自身高度和缺欠埋藏深度的测定。8.6.2对已发现的缺欠需要确定相对焊缝中心线的偏移量时，应进行平行扫查。8.6.3焊缝宽度较大或焊缝两侧母材厚度不相等且母材厚度相差8mm以上时应进行偏置非平行扫查。8.6.4对两侧母材厚度不等的焊缝进行非平行扫查时，宜使用单探头对进行多次扫查，见图9、图10。a）单面扫查时，应分别进行PCS1对中扫差、PCS2对中和偏置扫差。b）双面扫查时，应分别进行www.bzfxw.comPCS1、PCS2对中扫查。图9母材厚度不相等的焊缝检测非平面侧扫查方式图10母材厚度不相等的焊缝检测平面侧扫查方式8.6.5具有横向裂纹倾向的焊缝应增加横向非平行扫查，对已发现的横向缺欠需要确定缺欠在焊缝长度方向的位置时应进行纵向平行扫查。8.6.6特殊情况下，也可采用其他合适的扫查方式。8.7表面盲区8.7.1TOFD检测时扫查面和底面均存在表面盲区，盲区高度的计算参见附录C。8.7.2对于TOFD检测存在的表面盲区，宜通过采用窄脉冲宽频带探头、减少PCS值、改变探头参数和进行双面扫查等方法来减小盲区高度。8.7.3对于表面盲区的检测应采用磁粉检测、涡流检测或其他有效方法进行，检测和质量评定应执行相8标准分享网www.bzfxw.com免费下载 www.bzfxw.com DL/T330—20109.2.3对于直通波或底面反射波不可见或分区检测时，应采用对比试块进行深度校准。9.2.4深度校准应保证深度测量误差不大于工件厚度的1％，且不大于0.5mm。9.3位置编码器的校准9.3.1检测前和每工作4h应对位置编码器进行校准。9.3.2校准时应使扫查装置移动距离不小于500mm，检测设备所显示的位移与实际位移的误差不大于1％。9.4灵敏度设置9.4.1检测前应在对比试块或被检工件上设置检测灵敏度。9.4.2当采用对比试块上的衍射体设置灵敏度时，应将被检测厚度范围内较弱的衍射体信号波幅设置为满屏高的40％～80％，并在被检工件表面扫查时进行表面耦合补偿。9.4.3在被检工件上设置灵敏度时要求如下：a）一般将直通波的波幅设定到满刻度的40％～80％。b）当因工件表面状况的影响，不能利用直通波校准时，可将底面反射波幅设定为满刻度，再增益18dB～30dB。c）当工件厚度大于50mm时可用符合表1要求的横通孔的波幅设定到满刻度的40％～80％为起始灵敏度。d）当直通波和底面反射波均不可用时，可将材料的晶粒噪声设定为满刻度的5％～10％作为检测灵敏度。9.5检测设置和校准的复核9.5.1检测结束时或检测过程中每4h应对检测设置进行复核。9.5.2若初始设置和校准采用了对比试块，应在同一试块上进行复核。若在工件上设置和校准，应在工件上同一部位进行复核。www.bzfxw.com9.5.3若复核时发现检测设置和校准的参数偏离，则按表3的规定执行。表3偏离和纠正项目偏离量纠正措施≤6dB不需要采取措施，必要时可通过软件纠正灵敏度＞6dB应重新设置，并重新检测上次校准以来所检测的焊缝偏离≤0.5mm或板厚的2％不需要采取措施深度偏离＞0.5mm或板厚的2％应重新设置，并重新检测上次校准以来所检测的焊缝≤5％且不超过25mm不需要采取措施位移＞5％或超过25mm应重新设置，并对上次校准以来所检测的位置进行修正10检测10.1非平行扫查和偏置非平行扫查时应保证实际扫查路径与拟扫查路径一致，其最大偏差不超过PCS值的10％。10.2扫查速度应满足耦合和全波采集要求，最大不得超过50mm/s。10.3分段扫查时，相邻段扫查区的重叠范围应不小于25mm。10.4当直通波、底面反射波、材料晶粒噪声或波形转换波的波幅降低12dB以上或怀疑耦合不良时，应重新扫查该段区域；当直通波满屏或晶粒噪声波幅超过满屏高20％时，则应降低增益并重新扫查。10标准分享网www.bzfxw.com免费下载 DL/T330—201011检测数据分析11.1检测数据的有效性评定11.1.1分析数据之前，应对所采集的数据进行有效性评定。11.1.2数据丢失量不得超过每次扫查数据量的5％，且不允许相邻数据连续丢失。原始数据不得有修改、连接的痕迹。11.1.3扫查数据应保证声束足以覆盖检测区域，在分段扫查时其重叠范围应满足10.3的要求。11.1.4根据超声信号的相位判断缺欠的上下端点，若因信噪比太小而无法判断相位时，则检测数据无效。11.1.5若所获得数据无效，应采取纠正措施，重新进行扫查直至数据符合要求。11.2非相关显示的确定11.2.1对于有显示的TOFD图像应区分相关显示或非相关显示。11.2.2应按以下步骤确定非相关显示是由工件结构或者材料冶金结构的偏差所引起的：a）查阅加工和焊接文件资料。b）绘制衍射体的坐标，提供可显示出衍射体位置和表面不连续的横截面展示图。c）根据现有检测工艺规程对包含衍射体的区域进行验证。d）可辅助使用其他无损检测技术进行确定。11.2.3非相关显示应记录其位置和TOFD图像。11.3相关显示的分类11.3.1相关显示分为表面开口型缺欠显示、埋藏型缺欠显示和难以分类的显示。常见焊接缺欠TOFD图像参见附录D。11.3.2表面开口型缺欠显示可分为如下三类：a）扫查面开口型。该类型显示为直通波的减弱、消失或变形，且仅可观察到一个端点（缺欠下端点）产生的细长衍射信号。b）底面开口型。该类型显示为底面反射波的减弱、消失、延迟或变形，且仅可观察到一个端点（缺欠上端点）产生的细长衍射信号。c）穿透型。该类型显示为直通波和底面反射波同时减弱或消失，沿壁厚方向产生多处衍射信号。11.3.3埋藏型缺欠显示一般不影响直通波或底面反射波的信号。埋藏型缺欠显示可分为如下三类：a）点状显示。该类型显示为单个双曲线弧状，且与拟合弧形光标重合，无可测量长度和高度。b）细长显示。该类型显示为细长状，无可测量高度。c）长条状显示。该类型显示为长条状，可见上下两端产生的衍射信号，且靠近底面处端点产生的衍射信号与直通波同相位，靠近扫查面处端点产生的信号与底面反射波同相位。11.3.4对于难以按照11.3.2和11.3.3进行分类的显示，可采用其他检测方法进行进一步检测和分析。11.4缺欠位置测定11.4.1在X轴上位置的确定。根据位置编码器定位系统对缺欠沿焊缝的位置进行定位。11.4.2在Z轴上位置的确定。对于表面开口型缺欠显示，通常只有上或下端点的衍射波，通过判断其端点衍射波与直通波（或底面反射波）的相位关系确定其上（或下）端点，按附录C中式（3）计算或由仪器直接读出。11.4.3对于埋藏型缺欠显示，其上端点产生的衍射波与直通波反相且与底面反射波同相，通过测定缺欠端点的衍射波与直通波间的传播时间差t，按附录C中式（3）计算或由仪器直接读出。11.5缺欠尺寸测量11.5.1缺欠的尺寸由完全包含缺欠的矩形区域确定。缺欠的尺寸示意图见图12。缺欠的长度L为缺欠在扫查方向X轴的显示长度，缺欠的高度h为缺欠在焊缝厚度方向Z轴显示的尺寸。11 标准分享网www.bzfxw.com免费下载 DL/T330—201013缺欠评定13.1不允许存在的缺欠：a）裂纹、未熔合、未焊透等危害性的缺欠。b）表面开口缺欠。c）缺欠高度大于表4中h2的缺欠。d）缺欠高度小于等于h2时，不满足13.2和表4规定的缺欠。表4条状缺欠的评定mm埋藏性缺欠高度≤h2时，所允当长度超过Lmax时，埋藏焊缝类别厚度T许的单个缺欠的最大长度多个缺欠总长性缺欠最大允许高度h1Lmaxh21相邻两缺欠间距均不超过12≤T＜60T41一类焊缝36L的任何一组缺欠，其累计长T≥602052度在12T焊缝长度内不超过T2相邻两缺欠间距均不超过12≤T＜45T41二类焊缝33L的任何一组缺欠，其累计长T≥453052度在6T焊缝长度内不超过T注1：焊缝两侧母材厚度不同时，取薄侧厚度值。注2：表中L为该组缺欠中最长者的长度。注3：对于单个或多个缺陷高度h＜h1的线状缺欠，在任意12T范围内累计长度不得超过4T，且最大值为300mm。13.2单个点状缺欠显示每150mm焊缝长度内个数应小于等于N，N＝1.2T（T以mm为单位计）。13.3对于密集型点状显示，按条状显示处理。13.4相邻两条状缺欠显示在X轴方向间距小于其中较大的缺欠长度且在Z轴方向间距小于其中较大的缺欠高度时，应作为一条缺欠处理，以两缺欠长度之和作为其单个缺欠长度，高度之和作为其单个缺欠的高度(间距不计入缺欠尺寸）。单个条状缺欠和多个条状缺欠总长的评定按照表4进行。14检测记录和报告14.1检测记录和报告应至少包括如下内容：a）委托单位。b）被检工件，包括名称、编号、规格、材质、坡口型式、焊接方法和热处理状况、表面状态。c）检测设备，包括仪器、探头（探头种类、频率、角度、晶片尺寸等参数）、试块、耦合剂。d）检测工艺，包括探头布置、检测设置、校准方法、扫查方式、定位装置。e）检测部位、检测区域及相关显示的类型、位置、尺寸和分布应在草图上予以标明。f）检测数据，包括数据文件名称、缺欠位置与尺寸及缺欠部位TOFD图像。g）检测数据分析及结论。h）检测人员和责任人员签字及其技术资格。i）检测日期、报告日期。14.2检测报告格式可参见附录E。13 DL/T330—2010附录A（资料性附录）水电水利工程常用非合金钢、低合金钢和合金钢按主要质量等级分类按主要类别123特性分类普通质量优质特殊质量a）碳素结构钢。GB/T700中除普通质量A、B级钢以外a）优质碳素结构钢。GB/T的所有牌号及A、B级规定冷碳素结构钢。699中的65Mn、70Mn、70、75、成型性及模锻性特殊要求以规定最低强GB/T700中的Q21580、85钢。者。非合金钢度为主要特性的中A、B级，Q235b）保证淬火性钢。GB/T5216b）优质碳素结构钢。GB/T非合金钢的A、B级，Q275中的45H。699中除65Mn、70Mn、70、的A、B级c）保证厚度方向性能钢。75、80、85以外的所有牌号。GB/T5313中的所有非合金钢c）锅炉压力容器用钢。GB713中的Q245Ra）一般用途低合金结构钢。a）一般用途低合金结构钢。GB/T1591中的Q390E、Q345E、GB/T1591中的Q295B、Q345Q420和Q460。一般用途低合金（A级钢以外）和Q390(E级b）锅炉压力容器用低合金钢。可焊接合金高结构钢。GB/T1591低合金钢钢以外）。GB/T19189中的12MnNiVR，强度结构钢中的Q295、Q345b）锅炉压力容器用低合金GB3531中的所有牌号。牌号的A级钢钢。GB713除Q245以外的c）保证厚度方向性能低合金所有牌号钢。GB/T5313中的所有低合金钢牌号TMCP低合金结构钢GB/T19189中的07MnCrMoVR、07MnCrMoVDR。GB713中的合金钢（不锈钢、耐蚀和耐热钢除外）。可焊接合金高一般工程结构用合金钢GB5310中的合金钢。合金钢强度结构钢GB/T20933中的Q420bzGB/T16270中的高强度结构用调质钢板。高强度结构用TMCP钢。GB/T2087中的铁素体不锈钢和马氏体不锈钢14标准分享网www.bzfxw.com免费下载 DL/T330—2010附录B（资料性附录）参考试块B.1平底孔试块图B.1给出了平底孔试块的示例，有5个平底孔排在一直线上，孔径相同（φ1.5mm～3mm），孔底距探测面距离（深度）不同。借此可评定声能分布和分辨能力。孔深由最大到最小布置，可测试对表面开口缺欠和近表面缺欠的检测分辨力。另外也可测试厚板分区偏离焊缝中心线时的检测灵敏度。进行几次非平行扫查，每次探头分别偏离平底孔轴线一定增量，就可确定偏离轴线的灵敏度限值。若用多通道偏心扫查要求保证较宽区域（如焊缝加较宽热影响区）均可被声束覆盖，即可用该平底孔试块进行校验。该试块也可从机加工一面（即钻孔一面）进行扫查，检测表面开口缺欠的下端部衍射信号。图B.1平底孔参考试块B.2尖角槽试块图B.2给出了尖角槽试块的示例，槽的深度位置与上述平底孔试块相同，以60°V形槽作衍射体。槽宽一般为2mm～5mm，槽长10mm～20mm。V形槽通常用电火花加工。灵敏度可用V形槽尖端的衍射信号来校准。利用这种灵敏度衍射体的衍射信号，能更准确地对条形面状缺欠进行测深定高。图B.2尖角槽参考试块15 DL/T330—2010B.3横孔和切槽的组合试块图B.3给出了不同直径横孔和切槽的组合试块示例，该试块可用于调整灵敏度和分辨力。φ3mm设于厚度1/4、1/2和3/4位置。离探测面3mm处还钻有一φ2mm的横孔。切槽一般高1mm～2mm，长10mm～20mm，可用于测试底面分辨力。切槽宽度应尽可能窄些，最好＜1mm。整个试块尺寸应能确保PCS设置合适时探头对在扫查面上扫查。横孔深度位置形成的梯形差，应满足获得各横孔单独衍射信号的要求。图B.3不同直径横孔和切槽组合参考试块16标准分享网www.bzfxw.com免费下载 DL/T330—2010附录C（资料性附录）缺欠深度、高度及表面盲区高度的计算C.1假定探头中心间距为2S（S＝PCS/2），缺欠深度为d1，缺欠距焊缝中心线的偏移量为X，见图C.1。图C.1缺欠深度计算图根据几何关系，有：2222M+=−=Lctt(2)dSX+−()+dSX++()（C.1）011式中：c——波的传播速度，mm/μs；t——超声波在工件中传播的总时间，μs；t0——超声波在探头楔块中传播的时间，μs。假定缺欠位于焊缝中心线上，此时X＝0，所得d1值最小：22ctt(2)−02dS=−（C.2）14C.2若以直通波为参考起点，假定X＝0，则缺欠深度为：2tc+4tcSddd=（C.3）12式中：td——缺欠上端点的衍射波与直通波间的传播时间差，μs。同理可计算出缺欠下端点的深度d2。则缺欠的高度h为：h＝d2－d1C.3表面盲区高度计算。C.3.1扫查面盲区高度为：221/2Dc=+[/tS4]ct（C.4）SppC.3.2底面盲区高度为：2221/2D=+−−[(ctt)/4S]T（C.5）bpw式中：tp——直通波脉冲达到最高回波10％的时间，µs；tw——底面回波传播时间，µs；T——工件厚度，mm。17 标准分享网www.bzfxw.com免费下载 标准分享网www.bzfxw.com免费下载 DL/T330—2010附录E（资料性附录）焊缝衍射时差法超声检测报告报告编号：产品名称检测部位焊缝编号材料/规格坡口形式焊接方法表面状态检测时机检测仪器扫查方式设置1探头角度探头规格探头间距设置2探头角度探头规格探头间距校准方法试块位置编码器耦合剂质量标准工艺标准检测焊缝位置及缺陷位置示意图：缺欠缺欠缺欠位置（mm）缺欠尺寸（mm）评定图像编号编号性质结论XYdLh结论：检测/级别：校核/级别：年月日年月日22标准分享网www.bzfxw.com免费下载'